PP flame retardant masterbatch

1.  This is a compound flame retardant system,BDDP based by adding effective synergist and stabilizer. Dosage 8% will make the sample (3.0MM)achieve level UL94V0 ,compare with simple using BDDP it improved the flame retardant efficiency and reduced dosage of Sb2O3.

 

2.  Product Character:

Appearance:White loose powder

Br content:60%

Weight loss:≤0.3%

Melting point:110℃ Begin to softening and melting

Decomposition temperature:285℃,mass loss 5%:330℃

DissolubilityWater insoluble,Partly soluble in DichloroethaneToluene、Acetone Esters etc  
    T
oxicity LD50(Oral delivery in white mice)>5000mg/kg(non-toxic)   
    
Potential carcinogen :Non   
    
Skin irritation:Non
 

  • Comparison by using F68-112 in PP

 

 
Index table of comparisons
 
  Performance Powder of HOPP Powder of HOPP
(8%BDDP+Sb2O3)
Powder of HOPP(6%F68-112+Sb2O3) Powder of HOPP
(8%F68-112+Sb2O3)
1 Melt Index
(g/10min)
5.8 6.9 6.5 6.8
2 Tensile(Mpa) 31 30 31 30
3 Tensile nominal strain
(%)
 
79
 
70
 
73
 
71
4 Flexural modulus
(GPa)
1.1 1 1 1
5 Izod impact strength
(KJ/m*m)
A Type Gap
No gap
 


4.1
78.8
 


3.9
85.2
 


3.8
89
 


3.6
83
6 UL-94 Fire resistance
1.6mm
3.0mm
 
 
——
——


v-0
v-2


v-2
v-2


v-2
v-0